MIL-PRF-44103D
TABLE I. Requirements (continued)
Requirements
Classes 1 & 2
Classes 3 & 4
Characteristic
Min
Max
Min
Max
Hydrostatic Resistance (low pressure), cm
Initial
80
--
--
--
After weathering
65 3/
--
--
--
After cold crack (-20°F)
65 3/
--
--
--
Hydrostatic Resistance (high pressure), psi
Initial
--
--
300
--
After cold crack (-20°F)
--
--
250
--
After abrasion
--
--
250
--
Flame Resistance (5905) After flame, seconds:
Initial:
Warp
--
2
--
2
Filling
--
2
--
2
After weathering:
Warp
--
2
--
2
Filling
--
2
--
2
Consumption, percent:
Initial:
Warp
--
50
--
50
Filling
--
50
--
50
After weathering:
Warp
--
50
--
50
Filling
--
50
--
50
Melt-Drip:
Initial
4/
--
--
4/
After Weathering
4/
--
--
4/
Stiffness inch-pounds Initial:
Warp
--
0.020
--
--
Filling
--
0.020
--
--
At -20°F:
Warp
--
0.040
--
--
Filling
--
0.040
--
--
After heat aging:
Warp
--
0.040
--
--
Filling
--
0.040
--
--
Stiffness, cm, Warp only
At 70°F:
--
--
--
15
At 70°F after accelerated weathering:
--
--
--
15
At -20°F:
--
--
--
16
At -20°F after oven aging
--
--
--
16
Blocking at 200°F
--
--
--
No.2
Abrasion resistance:
2.5 5/
--
6/
--
Static slip resistance index units
At 73° F dry
--
--
7.0
--
At 73° F wet
--
--
7.0
--
1/ Requirement applies if a film or coating is applied to the surface of the cloth.
2/ Or equal to or better than the standard sample.
3/ The cloth shall not crack or flake.
4/ No specimen shall drop melted or flaming pieces.